FeCrAl 0Cr25Al5 kulîlka germkirinê ya sobeya elektrîkê ya germkirinê
Taybetmendiya sereke ya têl berxwedana germkirinê
| Tîpa Alloy | Çap (mm) | Berxwedan (μΩm) (20°C) | Tensile Qawet (N/mm²) | Dirêjbûn(%) | Bending Times | Max.Bedewam Xizmetkar Germahiya (°C) | Working Life (saet) |
| Cr20Ni80 | <0.50 | 1,09±0,05 | 850-950 | >20 | >9 | 1200 | >20000 |
| 0,50-3,0 | 1,13±0,05 | 850-950 | >20 | >9 | 1200 | >20000 | |
| >3.0 | 1,14±0,05 | 850-950 | >20 | >9 | 1200 | >20000 | |
| Cr30Ni70 | <0.50 | 1,18±0,05 | 850-950 | >20 | >9 | 1250 | >20000 |
| ≥0.50 | 1,20±0,05 | 850-950 | >20 | >9 | 1250 | >20000 | |
| Cr15Ni60 | <0.50 | 1,12±0,05 | 850-950 | >20 | >9 | 1125 | >20000 |
| ≥0.50 | 1,15±0,05 | 850-950 | >20 | >9 | 1125 | >20000 | |
| Cr20Ni35 | <0.50 | 1,04±0,05 | 850-950 | >20 | >9 | 1100 | >18000 |
| ≥0.50 | 1,06±0,05 | 850-950 | >20 | >9 | 1100 | >18000 | |
| 1Cr13Al4 | 0.03-12.0 | 1,25±0,08 | 588-735 | >16 | >6 | 950 | >10000 |
| 0Cr15Al5 | 1,25±0,08 | 588-735 | >16 | >6 | 1000 | >10000 | |
| 0Cr25Al5 | 1,42±0,07 | 634-784 | >12 | >5 | 1300 | >8000 | |
| 0Cr23Al5 | 1,35±0,06 | 634-784 | >12 | >5 | 1250 | >8000 | |
| 0Cr21Al6 | 1,42±0,07 | 634-784 | >12 | >5 | 1300 | >8000 | |
| 1Cr20Al3 | 1,23±0,06 | 634-784 | >12 | >5 | 1100 | >8000 | |
| 0Cr21Al6Nb | 1,45±0,07 | 634-784 | >12 | >5 | 1350 | >8000 | |
| 0Cr27Al7Mo2 | 0.03-12.0 | 1,53±0,07 | 686-784 | >12 | >5 | 1400 | >8000 |
| NAV | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| KÎMYAYA SEREKE | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26,5-27,8 |
| Al | 4.0-6.0 | 4,5-6,5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| PÊKIRIN | Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rehetî | Rehetî | Rehetî | Rehetî | Rehetî | Rehetî | Rehetî | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Germahiya herî zêde (oC) | 650 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| BERXWEDANA20oC (μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| DENSITY(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| HEAT CHANGE | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
| RATE(KJ/m·h·oC) | ||||||||
| rêjeya berfirehbûnê (α×10-6/oC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| xala helînê (oC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| hêza vekêşanê (N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| dirêjbûn(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| guhertina herêmê (%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Frekansa bendkirinê (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| hişkbûn (HB) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| avahiya mîkrografîk | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| milkê magnetîkî | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
| Dirêj (mm) | Tolerans (mm) | Dirêj (mm) | Tolerans (mm) |
| 0,03-0,05 | ±0.005 | >0,50-1,00 | ±0.02 |
| >0,05-0,10 | ±0.006 | > 1.00-3.00 | ±0.03 |
| >0,10-0,20 | ±0.008 | > 3.00-6.00 | ±0.04 |
| >0,20-0,30 | ±0.010 | > 6.00-8.00 | ±0.05 |
| >0,30-0,50 | ±0.015 | > 8.00-12.0 | ±0.4 |
| Stûrahî (mm) | Tolerans (mm) | Firahî (mm) | Tolerans (mm) |
| 0,05-0,10 | ±0.010 | 5.00-10.0 | ±0.2 |
| >0,10-0,20 | ±0.015 | > 10.0-20.0 | ±0.2 |
| >0,20-0,50 | ±0.020 | > 20.0-30.0 | ±0.2 |
| >0,50-1,00 | ±0.030 | >30.0-50.0 | ±0.3 |
| > 1.00-1.80 | ±0.040 | > 50,0-90,0 | ±0.3 |
| > 1,80-2,50 | ±0.050 | > 90.0-120.0 | ±0.5 |
| > 2.50-3.50 | ±0.060 | > 120.0-250.0 | ±0.6 |
I Em hilberînerê têlên berxwedana germkirinê ne
Têl FeCrAL, têl NiCr, têl CuNi:
II Awantaj û Serlêdan
A. Parametreya laşî:
1) Dirêjahiya têl: 0,025 ~ 15 mm
2) Nîkelê paqij xwedan şiyana ku li ber germahiyên bi nisbeten bilind bêyî xirabûnê radiweste.Operasyona herî zêde
germahî nêzîkî 600 ° C ye
3) Têlê nîkel di avakirina yek hêl an pir-strand de heye.Ew ji stokê an tazî, an îzolekirî tê peyda kirin
B. Taybetmendî:
1) Rasthatina hêja
2) Rewşa rûbera yekgirtî û bedew bê deq
3) Kapasîteya çêker a kulikê ya hêja
C. Serîlêdanên sereke û armanca gelemperî:
1) Ev têl di heman demê de dikare bi gelemperî ji bo kapikên transîstor, anodes ji bo lûleyên elektronîkî têne destnîşan kirin bi berfirehî were bikar anîn,
lîreyên hêmanên elektronîkî / tîrêjên tîrêjê ji bo lampe û ji bo têl-mesh.Di heman demê de di forma strip de ji bo cûrbecûr tê bikar anîn
sepanên di nav de bataryayên Ni-Cd
2) Di heman demê de ji bo kabloyan, Lead-in-Wire ji bo lampe, piştgirên lûleyên elektronîkî, pêlên girêdana elektrîkî yên qumaşê têl tê bikar anîn.
li cihê ku germahî ji yên ku sifir jê re guncaw e zêdetir be, tevndana têl
3) Serîlêdanên tîpîk ev in: qedandina hêmanên germkirinê yên wekî di sobeyan, extruderên plastîk, sobeyan de.
Di pîşesaziya ronahiyê de têlên fîlament piştgirî û pêşeng in